Application of Calcium Silicate Insulation Board:
Aluminium and non-ferrous metal foundries
Steel and iron foundries
Heat treatment plants
Industrial furnaces and furnace construction
Machine and plant construction
Domestic fire places and chimneys
Glass and ceramics industry
On-shore and off-shore fire protection
Engineering
Aluminium and non-ferrous metal foundries
Steel and iron foundries
Heat treatment plants
Industrial furnaces and furnace construction
Machine and plant construction
Domestic fire places and chimneys
Glass and ceramics industry
On-shore and off-shore fire protection
Engineering
4o
Items | Unit | FCS-50 | FCS-85C Carbon Fiber Reinforced |
FCS-85G Glass Fiber Reinforced |
Bulk Density | Kg/m3 | 500±10% | 850 ±10% | 850 ±10% |
Bending Strength | MPa | ≥ 4.0 | 6 | 5 |
Compression Strength At 5% Deformation At Break |
MPa | ≥ 5.0 | 11 | 10 |
— | 15 | 12 | ||
Continuous Service Temp. | ℃ | 1000 | 850 | 850 |
Linear Shrinkage 650℃x24h, % | Linear | — | 0.1 | 0.15 |
Thickness | — | 0.6 | 0.86 | |
Linear Shrinkage 700℃x24h, % | Linear | — | 0.18 | 0.25 |
Thickness | — | 0.8 | 1 | |
Linear Shrinkage 750℃x24h, % | Linear | — | 0.2 | 0.28 |
Thickness | — | 0.9 | 1.1 | |
Linear Shrinkage 850℃x24h, % | Linear | — | 0.21 | 0.35 |
Thickness | — | 1.1 | 1.3 | |
Linear Shrinkage 1000℃x24h, % | Linear | ≤1.5 | 0.36 | 0.49 |
Thickness | 1000℃x3h | 2.4 | 3.5 | |
Thermal Conductivity W/m.K | 100℃ | — | 0.103 | 0.113 |
200℃ | — | 0.114 | 0.12 | |
300℃ | ≤0.110 | 0.124 | 0.121 | |
400℃ | — | 0.133 | 0.125 | |
Chemical Analysis % | SiO2 | ≥ 48 | 49-52 | 49-52 |
CaO | ≥ 38 | 39-42 | 39-42 | |
Al2O3 | ≤ 1 | 0.4-0.5 | 0.4-0.5 | |
Fe2O3 | ≤ 0.5 | 0.3-0.4 | 0.3-0.4 | |
Surface Condition | Double sanded; four side can be cut upon request. (FCS-50 need collect Extra Charge) |